Bond strength evaluation of four adhesive systems to dentin in vitro

Xiao Ximei1，2, Xing Lu3, Xu Haiping1，2, Jiang Zhe1，2, Su Qin1，

1. State Key Laboratory of Oral Diseases, Sichuan University, Chengdu 610041, China; 2.Dept. of Endodontics, West China School of Stomatology, Sichuan University, Chengdu 610041, China; 3. Dept. of Endodontics, Tianjin Stomatological Hospital, Tianjin 300041, China

Received:2011-09-19 Revised:2012-03-09 Online:2012-08-01 Published:2012-08-01

摘要/Abstract

摘要：

目的比较4种粘接剂对牙本质的粘接强度，并观察粘接界面，评估其抗力性能。方法采用Prime & BondNT（PBNT）、Tetric N-Bond（TNB）、Clearfil SE Bond（CSEB）、G Bond（GB）4种粘接剂粘接树脂于离体下颌第三磨牙的咬合面和近中面，近中面进行剪切力实验，记录断裂峰值；咬合面部分进行微拉伸粘接强度（TBS）测定，扫描电镜观察粘接界面形态。结果在剪切力实验中，PBNT与TNB的抗剪切粘接强度（SBS）最大，两者间差异无统计学意义（P>0.05）。PBNT的SBS高于CSEB与GB（P<0.05）；TNB的SBS高于GB（P<0.05），与CSEB的强度差异无统计学意义（P>0.05）。与剪切力实验结果一致，PBNT和TNB的TBS高于CSEB和GB（P<0.05）。扫描电镜下，PBNT和TNB的树脂突比较细长，粘接层较厚；CSEB树脂突短小，GB树脂突更加稀疏。结论全酸蚀粘接剂的粘接强度较自酸蚀粘接剂高，一步法自酸蚀粘接剂强度最低；粘接剂的界面形态与粘接强度存在一定程度的关联性。

关键词: 牙本质, 粘接, 酸蚀, 微拉伸粘接强度, 抗剪切粘接强度

Abstract:

Objective To compare the adhesive strength and observe the bonding interface. According to statistic analysis and scanning electron microscope（SEM） observation, the resistance capacity of four adhesive systems is evaluated. Methods Prime & Bond NT（PBNT）, Tetric N-Bond（TNB）, Clearfil SE Bond（CSEB）, G Bond（GB） were bonded to the occlusal surfaces and mesial surfaces of third molars respectively. The mesial resins received shear force experiment and the fracture load were recorded. The tensile bond strength（TBS） of the remaining parts were tested. The interfacial configuration were observed under SEM. Results In the shear bond strength（SBS） experiment, PBNT and TNB showed the best result, but there was no significant difference between them（P>0.05）. The SBS of PBNT was stronger than that of CSEB and GB（P<0.05）. The SBS of TNB was stronger than that of GB（P<0.05）. There was no
significant difference between TNB and CSEB（P>0.05）. In accordance with the shear force result, the TBS of PBNT and TNB was larger than CSEB and GB（P<0.05）. Under SEM, resin tags of PBNT and TNB were longer and slender, the bonding layer was thick. Resin tags of CSEB were shorter, the ones of GB were the fewest and shortest. Conclusion Compared to self-etching system, total-etching system could reach better bonding strength. There is some connection between the interfacial configuration of adhesives and bond strength of them.

Key words: dentin, adhesive, etching, tensile bond strength, shear bond strength

肖喜梅1，2 邢路3 许海平1，2 江喆1，2 苏勤1，2. 4种粘接剂对牙本质粘接强度的体外评价[J]. 华西口腔医学杂志, 2012, 30(4): 343-345.

Xiao Ximei1，2, Xing Lu3, Xu Haiping1，2, Jiang Zhe1，2, Su Qin1，. Bond strength evaluation of four adhesive systems to dentin in vitro[J]. West China Journal of Stomatology, 2012, 30(4): 343-345.

[1]	侯玮玮, 郑绪红, 陈晓玲, 蔡蔚靓, 王朝阳, 苏智伟, 赵鹃. 数字化技术在酸蚀症伴重度磨耗患者功能美学缺陷修复中的应用1例[J]. 华西口腔医学杂志, 2024, 42(1): 111-120.
[2]	达尔亚·俄尼木拜, 张迪, 古丽努尔·阿吾提. 脱矿牙本质基质和脱细胞牙本质基质成骨效果的对比研究[J]. 华西口腔医学杂志, 2024, 42(1): 28-36.
[3]	王梓, 薛明. 4种机用镍钛锉根管预备后形成牙本质微裂的研究[J]. 华西口腔医学杂志, 2024, 42(1): 75-81.
[4]	朱建宇, 洪菲菲, 何良航, 温玮, 雷贤林, 张志升, 尹路. Er: Yag激光拆除3种材质贴面的实验研究[J]. 华西口腔医学杂志, 2023, 41(5): 568-572.
[5]	王宗华, 张晓冉, 姚烁, 赵家鑫, 周传健, 吴峻岭. 冷热循环对新型低收缩树脂粘接剂粘接性能的影响[J]. 华西口腔医学杂志, 2023, 41(3): 276-283.
[6]	王丽, 吴菲, 肖墨, 陈雨欣, 吴丽更. 基于深度学习的龋源性牙髓炎露髓风险预测[J]. 华西口腔医学杂志, 2023, 41(2): 218-224.
[7]	商梦瑶, 魏雨奇, 于美娇, 张瑾, 崔平平. 视神经炎患者激素治疗引起牙酸蚀症1例[J]. 华西口腔医学杂志, 2023, 41(2): 243-246.
[8]	孟雨晨, 黄帆, 王思霖, 黄欣, 逯宜, 裴丹丹. 羟磷灰石牙本质脱敏剂对温和型通用型粘接系统粘接性能研究[J]. 华西口腔医学杂志, 2022, 40(6): 668-675.
[9]	龚佳明, 张启航, 苟萍, 王辉, 余佳颖, 余占海. 自体牙本质用于牙槽嵴增量的Meta分析[J]. 华西口腔医学杂志, 2022, 40(5): 566-575.
[10]	贺锦秀, 高静, 刘春煦, 解晨阳, 余嘉怡, 于海洋. 一种序列3D打印导板引导的瓷贴面分区粘接技术[J]. 华西口腔医学杂志, 2022, 40(3): 365-369.
[11]	林琪, 林昱, 谢云德, 马忠雄. 原子力显微镜分析激光消融对牙本质表面微纳米结构的影响[J]. 华西口腔医学杂志, 2022, 40(2): 155-161.
[12]	韩安鹏, 鲁方丽, 陆玉平, 李强, 陈栋. Micro-CT对遗传性牙本质发育缺陷离体患牙的特征研究[J]. 华西口腔医学杂志, 2022, 40(2): 162-168.
[13]	王莹, 杨家雪, 谢海峰, 陈晨. 充填厚度对光固化大块复合树脂充填效果的影响[J]. 华西口腔医学杂志, 2022, 40(2): 169-174.
[14]	汤皓, 朱亚文, 朱家祥, 李全利. 三斜磷钙石糊剂封闭牙本质小管的体外研究[J]. 华西口腔医学杂志, 2021, 39(6): 667-674.
[15]	徐英新, 李稳, 苏敏. 2种抗氧化剂恢复漂白后釉质粘接强度的研究[J]. 华西口腔医学杂志, 2021, 39(4): 453-457.

4种粘接剂对牙本质粘接强度的体外评价

Bond strength evaluation of four adhesive systems to dentin in vitro

RichHTML

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价