Abstract:

Objective This study aims to investigate bond strength between zirconia and resin cement through surface treatments with Er: YAG laser, Nd: YAG laser, and Si-Zr coating. Methods Seventy-five round pre-sintered zirconia discs with a diameter of 18 mm and a thickness of 1.5 mm were prepared by a powder compactor. Fifty discs were randomly divided into five groups of 10 discs each and were subjected to five surface treatments: no treatment (control group), sandblasting with alumina particles (sandblasting group), Er: YAG laser treatment (Er: YAG laser group), Nd:YAG laser treatment (Nd: YAG laser group), and Si-Zr coating treatment (Si-Zr coating group). The discs were then bonded to composite resin columns with resin cement. The shear bond strength of each group was tested with a universal tester. Roughness tester, scanning electron microscope (SEM), and energy dispersive spectroscopy were used to analyze surface performance. Results The bond strength of the Si-Zr coating group was higher than that of the remaining groups (P<0.05). The difference in bond strength between the sandblasting group and the Er: YAG laser group was not statistically significant (P>0.05), but both of them had higher bond strength than the Nd: YAG laser group (P<0.05). The Si-Zr coating group had the highest surface roughness (P<0.05). The surface roughness of the sandblasting, Er: YAG laser, and Nd: YAG laser groups was higher than that of the control group (P<0.05), but the difference among the three groups was not statistically significant (P>0.05). SEM observations showed irregular scratches on the surface of the sandblasting group and large pits with holes on the surface of the Er: YAG and Nd: YAG laser groups. In the Er: YAG laser group, the crystal structure was replaced by a smooth surface with a large amount of microcracks due to partial melting. Complex porous structures that comprised “island-like” structures and mass pores among the grains were observed on the surface of the Si-Zr coating. Only Zr, O, and Y were detected on the surfaces of the control, Er: YAG laser, and Nd: YAG laser groups. Al was found on the surface of the sandblasted group, and a higher proportion of Si was detected on the surface of the Si-Zr coating group. Conclusion Er: YAG laser and Nd: YAG laser treatment on the zirconia ceramic surface could increase roughness and improve the bond strength to resin cement. Si-Zr coating treatment is an effective alternative for increasing the roughness and bond strength of zirconia surface and is superior to sandblasting and laser treatments.

Key words: zirconia, surface treatment, bond strength, laser, coating