铒,铬:钇钪镓石榴石激光切割牙体硬组织效果的扫描电子显微镜观察

华西口腔医学杂志

铒,铬:钇钪镓石榴石激光切割牙体硬组织效果的扫描电子显微镜观察

于静涛,贾兴亚,乔丽艳,王雪梅,包穆蓉

110002　中国医科大学口腔医院口腔内科

收稿日期:2003-10-25 修回日期:2003-10-25 出版日期:2003-10-20 发布日期:2003-10-20
基金资助:
本课题为辽宁省科委重大科研项目基金资助(编号94129005)

A Scanning Electron Microscopy Study on Morphological Changes of Er,Cr:YSGG Laser-Cutted Dental Hard Tissue

YUJingtao,JIAXingya,QIAO Liyan,et al.

Department ofOral Medicine,College ofStomatology,China Medical University, Shenyang110002,China

Received:2003-10-25 Revised:2003-10-25 Online:2003-10-20 Published:2003-10-20

摘要/Abstract

摘要：

目的　对铒,铬:钇钪镓石榴石(Er,Cr:YSGG)激光切割的牙体硬组织进行扫描电子显微镜观察,探讨此激光在不同能量参数下进行窝洞制备的效果,以便为其在临床上的应用与推广提供实验依据。方法　将12颗前磨牙随机分3组,分别用高速裂钻、4W Er,Cr:YSGG激光及6W Er,Cr:YSGG激光处理后,将牙齿沿横向、纵向剖开,常规制片,扫描电镜观察牙体硬组织表面结构形态。结果　钻切组:切面较平,但有明显裂纹;表面覆盖致密的玷污层。激光组:切面不平,呈鱼鳞状改变,无玷污层;牙本质切面小管清晰,无炭化及热损伤改变。与4 W功率相比,6 W时表面更为粗糙。结论　应用Er,Cr:YSGG激光切割后的牙体,其表面结构有助于修复材料与牙体组织间的粘接。建议临床应用时采用高能量参数切割牙釉质,低能量参数切割牙本质。

关键词: 铒,铬:钇钪镓石榴石激光, 牙体硬组织, 扫描电子显微镜

Abstract:

Objective　The purpose of this studywas to evaluate the morphological changes of Er,Cr:YSGG laser irradiat- ed dental hard tissues by scanning electron microscopy (SEM).Methods　12 freshly extracted premolarswere treatedwith fissure bur, Er,Cr:YSGG laser at 4 watt, Er,Cr:YSGG laser at 6 watt, respectively, and then bisected transversally and longitudinally. The tooth slice were prepared with conventional methods and observed by SEM.Results　Compared with fissure bur, laser treat- ment resulted in a rather scaly and rough surface. The sectionswere free of smear layer, with open dentinal tubules. No carboniza- tion and thermal damages were observed. The laser at 6 watt appeared rougher than at 4 watt, occasionally caused micro-cracks. Conclusion　The utilizing of Er,Cr:YSGG laser can contribute to enhance the bond strength between restorative materials and dental hard tissues. It suggests that higher energy could be applied in cutting enamel, whereas the lower energy in dentin.

Key words: Er,Cr:YSGG laser, dental hard tissue, scanning electron microscopy

于静涛,贾兴亚,乔丽艳,王雪梅,包穆蓉. 铒,铬:钇钪镓石榴石激光切割牙体硬组织效果的扫描电子显微镜观察[J]. 华西口腔医学杂志.

YUJingtao,JIAXingya,QIAO Liyan,et al.. A Scanning Electron Microscopy Study on Morphological Changes of Er,Cr:YSGG Laser-Cutted Dental Hard Tissue[J]. West China Journal of Stomatology.

[1]	向科臻, 陈亮, 杨德琴. 基于聚酰胺—胺树枝状聚合物的牙体硬组织仿生再矿化的研究进展[J]. 华西口腔医学杂志, 2020, 38(6): 692-696.
[2]	李燕梅包广洁钟妮吕玮张文霞王兰兰康宏. 山羊颞下颌关节盘胶原构筑和生物力学性能研究[J]. 华西口腔医学杂志, 2016, 34(1): 73-77.
[3]	台银霞朱宪春闫森刘畅张娴史学明. 不同处理方法对瓷表面微观形貌的影响[J]. 华西口腔医学杂志, 2013, 31(1): 57-60.
[4]	林金莹姚江武林昌健. 加速老化对光固化复合树脂色度和显微结构的影响[J]. 华西口腔医学杂志, 2008, 26(03): 291-295.
[5]	王志凌,肖晓蓉,周学东,彭雪梅,廖运茂. 对氨基苯甲酸对牙龈卟啉单胞菌细胞形态影响的扫描电镜观察[J]. 华西口腔医学杂志, 2003, 21(04): 277-280.