渗透树脂与前牙美学树脂颜色稳定性的比较研究

doi:10.7518/hxkq.2019.03.008

华西口腔医学杂志 ›› 2019, Vol. 37 ›› Issue (3): 270-274.doi: 10.7518/hxkq.2019.03.008

渗透树脂与前牙美学树脂颜色稳定性的比较研究

张润荃¹,李大军^1,²,赵晓一¹()

1.北京大学口腔医学院·口腔医院综合科国家口腔疾病临床医学研究中心口腔数字化医疗技术和材料国家工程实验室口腔数字医学北京市重点实验室,北京 100081
2.裕华美诺口腔诊所,石家庄 050000

收稿日期:2018-12-12 修回日期:2019-03-22 出版日期:2019-06-01 发布日期:2019-06-12
通讯作者: 赵晓一 E-mail:xiaoyi_zhao@bjmu.edu.cn
作者简介:张润荃,主治医师,学士,E-mail:rq_zhang@139.com
基金资助:
北京大学口腔医学院科研基金(PKUSS20130203)

Evaluation of the color stability of infiltrant resin in comparison to aesthetic composite resins

Runquan Zhang¹,Dajun Li^1,²,Xiaoyi Zhao¹()

1.Dept. of General Dentistry, Peking University School and Hospital of Stomatology & National Clinical Research Center for Oral Diseases & National Engineering Laboratory for Digital and Material Technology of Stomatology & Beijing Key Laboratory of Digital Stomatology, Beijing 100081, China
2.Yuhua Meinuo Dental Clinic, Shijiazhuang 050000, China

Received:2018-12-12 Revised:2019-03-22 Online:2019-06-01 Published:2019-06-12
Contact: Xiaoyi Zhao E-mail:xiaoyi_zhao@bjmu.edu.cn
Supported by:
The Youth Fund Clinical Program of Peking University School of Stomatology(PKUSS20130203)

摘要/Abstract

摘要：

目的通过分析不同树脂材料对饮料色素的着色效果,比较渗透树脂与前牙美学树脂颜色稳定性的差异。方法选择3种前牙美学树脂（Filtek Z250、Filtek Z350 XT、Beautiful Flow Plus F00）及人工早期龋渗透树脂（Icon）处理样本各20例,不同树脂样本分别分为2组（每组10例）分别置于咖啡溶液及蒸馏水中浸泡1、2、3周。应用Crystaleye分光光度比色仪进行样本颜色分析。结果人工早期龋渗透树脂处理表面的着色明显高于其他前牙美学树脂（P<0.05）。所有实验树脂及渗透树脂处理表面的着色均随时间延长而增加,但第1周的着色最为显著,明显高于第2周及第3周的着色（P<0.05）。结论人工早期龋渗透树脂处理表面较前牙美学树脂更易发生颜色改变。

关键词: 渗透树脂, 复合树脂, 颜色稳定性

Abstract:

Objective To investigate the color stability of infiltrant resin together with three other composites exposed to staining solution. Methods Three types of anterior aesthetic composite resins (Filtek Z250, Filtek Z350 XT, and Beautiful Flow Plus F00) and artificial caries with Icon infiltrant resin were used. The samples were randomly divided into two groups (each contained 10 specimens): coffee solution and distilled water immersion for three weeks. Color parameters were determined with the Crystaleye spectrophotometer. Results Artificial caries lesions infiltrated by Icon showed much higher ΔE than those infiltrated by other aesthetic resins (P<0.05). The discoloration of all the experimental resins and the artificial caries infiltrated with Icon increased with time, but the discoloration on the 1 ^st week was significantly higher than those on the 2 ^nd and 3 ^rd weeks. Conclusion Artificial caries infiltrated with Icon was more vulnerable and susceptive to food color than those infiltrated with other aesthetic composite resins.

Key words: infiltrant resin, composite resin, color stability

中图分类号:

张润荃,李大军,赵晓一. 渗透树脂与前牙美学树脂颜色稳定性的比较研究[J]. 华西口腔医学杂志, 2019, 37(3): 270-274.

Runquan Zhang,Dajun Li,Xiaoyi Zhao. Evaluation of the color stability of infiltrant resin in comparison to aesthetic composite resins[J]. West China Journal of Stomatology, 2019, 37(3): 270-274.

图/表 3

表 1

图 1

表 2

参考文献 13

[1]	Paris S, Meyer-Lueckel H . Infiltrants inhibit progression of natural caries lesions in vitro[J]. J Dent Res, 2010,89(11):1276-1280. doi: 10.1177/0022034510376040 URL
[2]	Meyer-Lueckel H, Bitter K, Paris S . Randomized controlled clinical trial on proximal caries infiltration: three-year follow-up[J]. Caries Res, 2012,46(6):544-548. doi: 10.1159/000341807 URL
[3]	Torres C, Borges A . Color masking of developmental enamel defects: a case series[J]. Oper Dent, 2015,40(1):25-33. doi: 10.2341/13-346-T URL
[4]	隋小玲, 刘源, 杨燃 , 等. 奥乐V护牙剂对早期釉质龋再矿化作用的研究[J]. 华西口腔医学杂志, 2013,31(2):141-144, 149. doi: 10.7518/hxkq.2013.02.007
	Sui XL, Liu Y, Yang R , et al. Effect of OHOLV on the remineralization of early enamel caries[J]. West China J Stomatol, 2013,31(2):141-144, 149. doi: 10.7518/hxkq.2013.02.007
[5]	Gray GB, Shellis P . Infiltration of resin into white spot caries-like lesions of enamel: an in vitro study[J]. Eur J Prosthodont Restor Dent, 2002,10(1):27-32. URL pmid: 12051129
[6]	Ghinea R, Pérez MM, Herrera LJ , et al. Color difference thresholds in dental ceramics[J]. J Dent, 2010,38(Suppl 2):e57-e64. doi: 10.1016/j.jdent.2010.07.008 URL
[7]	Yew HZ, Berekally TL, Richards LC . A laboratory investigation of colour changes in two contemporary resin composites on exposure to spices[J]. Aust Dent J, 2013,58(4):468-477. doi: 10.1111/adj.2013.58.issue-4 URL
[8]	Shah MB, Ferracane JL, Kruzic JJ . R-curve behavior and toughening mechanisms of resin-based dental composites: effects of hydration and post-cure heat treatment[J]. Dent Mater, 2009,25(6):760-770. doi: 10.1016/j.dental.2008.12.004 URL pmid: 19187956
[9]	Mair LH . Staining of in vivo subsurface degradation in dental composites with silver nitrate[J]. J Dent Res, 1991,70(3):215-220. doi: 10.1177/00220345910700031201 URL
[10]	Paris S, Hopfenmuller W, Meyer-Lueckel H . Resin infiltration of caries lesions: an efficacy randomized trial[J]. J Dent Res, 2010,89(8):823-826. doi: 10.1177/0022034510369289 URL
[11]	Venturini D, Cenci MS, Demarco FF , et al. Effect of polishing techniques and time on surface roughness, hardness and microleakage of resin composite restorations[J]. Oper Dent, 2006,31(1):11-17. doi: 10.2341/04-155 URL
[12]	Mueller J, Yang F, Neumann K , et al. Surface tridimensional topography analysis of materials and finishing procedures after resinous infiltration of subsurface bovine enamel lesions[J]. Quintessence Int, 2011,42(2):135-147.
[13]	Ulrich I, Mueller J, Wolgin M , et al. Tridimensional surface roughness analysis after resin infiltration of (deproteinized) natural subsurface carious lesions[J]. Clin Oral Investig, 2015,19(6):1473-1483. doi: 10.1007/s00784-014-1372-5 URL

实验树脂	生产厂家	有机基质	填料及其直径	填料质量比/体积比（%）
Icon	德国DMG公司	TEGDMA	-	-
Filtek Z250	美国3M ESPE公司	Bis-GMA;UDMA;Bis-EMA	氧化锆/二氧化硅（0.01~3.5 μm）	82/60
Filtek Z350XT	美国3M ESPE公司	Bis-GMA;UDMA;TEGD-	二氧化硅（20 nm）;氧化锆（4~	78.5/63.3
		MA;PEGDMA;Bis-EMA	11 nm）;二氧化硅/氧化锆颗粒团
			聚体（20 nm及4~11 nm）
Beautiful Flow Plus F00	日本Shofu公司	Bis-GMA;TEGDMA	氟铝硼硅酸盐玻璃和Al₂O₃（0.01~	67.3/47.0
			4.0 μm）

实验树脂	分组	1周	2周	3周
Icon	组1	11.8±3.5	13.1±3.8	14.4±4.1
	组2	1.7±0.4	2.6±0.4	3.1±0.3
Filtek Z250	组1	3.1±0.5	3.9±0.6	4.5±0.7
	组2	0.8±0.2	1.2±0.2	1.7±0.3
Filtek Z350XT	组1	3.8±0.5	4.9±0.7	5.8±0.4
	组2	1.2±0.3	1.7±0.4	2.1±0.4
Beautiful Flow Plus F00	组1	4.0±1.1	5.5±1.2	6.3±1.1
	组2	0.8±0.1	1.2±0.2	1.8±0.2

[1]	罗文佶, 黄文凯, 徐明华, 任玲, 程玉瑶, 战德松, 付佳乐. 10种复合树脂颜色稳定性与吸水溶解性研究[J]. 华西口腔医学杂志, 2023, 41(1): 58-66.
[2]	薛晶. 大块充填树脂的临床应用影响因素[J]. 华西口腔医学杂志, 2020, 38(3): 233-239.
[3]	薛晶, 杨壁娜. 复合树脂预热的研究现状和临床应用[J]. 华西口腔医学杂志, 2019, 37(6): 571-576.
[4]	刘清,杨玉琼,聂蓉蓉,孟翔峰. 牙本质玷污层特性对自粘接树脂水门汀粘接强度的影响[J]. 华西口腔医学杂志, 2018, 36(6): 619-622.
[5]	吴峻岭,李彤,高旭,张强,刘迪,葛建华,周传健. 水中浸泡对自修复抗菌复合树脂性能影响的实验研究[J]. 华西口腔医学杂志, 2018, 36(5): 521-527.
[6]	吴峻岭,张强,孙睿男,朱婷,葛建华,周传健. 含长链烷基季铵盐纳米抗菌无机填料的复合树脂对人牙菌斑生物膜的影响[J]. 华西口腔医学杂志, 2015, 33(6): 565-569.
[7]	陈智陈彬文. 根管治疗后牙体修复的治疗方案选择[J]. 华西口腔医学杂志, 2015, 33(2): 115-120.
[8]	王立凯刘亚男郑焱李萍萍. 人工老化对不同厚度瓷聚体及不同类型树脂黏固材料颜色稳定性的影响[J]. 华西口腔医学杂志, 2015, 33(2): 201-205.
[9]	吴峻岭周凯运朱婷周传健. 含长链烷基季铵盐的纳米抗菌无机填料的合成及其在牙科复合树脂中的应用研究[J]. 华西口腔医学杂志, 2014, 32(5): 513-518.
[10]	刘杰吴皓孟凡玉宋春花. 3种偶联剂对铸造纯钛与硬质复合树脂结合强度的影响[J]. 华西口腔医学杂志, 2014, 32(3): 225-228.
[11]	赵晓一高学军. 渗透树脂治疗对釉质白斑样病损颜色的影响[J]. 华西口腔医学杂志, 2014, 32(3): 306-309.
[12]	冯朝华刘荣芳赵奇楚小玉. 渗透树脂对前牙唇面白垩斑治疗效果的临床评价[J]. 华西口腔医学杂志, 2013, 31(6): 597-599.
[13]	刘永红葛立宏陈惠珍. 渗透树脂对乳、恒磨牙邻面早期龋损渗透能力的对比研究[J]. 华西口腔医学杂志, 2013, 31(2): 161-164.
[14]	刘永红1 葛立宏2 陈慧珍1 池学谦1. 渗透树脂在自然形成的早期龋损中渗透能力的研究[J]. 华西口腔医学杂志, 2012, 30(5): 483-486.
[15]	吴峻岭1 金婵媛1 聂晓萌1 周凯运2 周传建2. 新型纳米抗菌无机填料的合成及其抗菌性能的初步研究[J]. 华西口腔医学杂志, 2012, 30(5): 526-529.

渗透树脂与前牙美学树脂颜色稳定性的比较研究

Evaluation of the color stability of infiltrant resin in comparison to aesthetic composite resins

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 3

参考文献 13

相关文章 15

编辑推荐

Metrics

本文评价