关键词: 树脂核, 表面处理, 玻璃离子水门汀, 剪切粘接强度

Abstract:

Objective  To compare shear bond strength（SBS） between composite resin core（CRC） disposed with three different surface treatments and glass ionomer cement（GIC）, so that to provide theoretical basis for luting of crowns to CRC. Methods  According to three different surface treatments, thirty blocks of CRC were randomly and equally divided into three groups: Roughening with diamond grit bur（RDB）, RDB plus etching with GlumaR Etch 35 Gel （RDBE）, RDB plus coating with AdperTM Single Bond2 adhensive（RDBA）. All CRC were cemented with GIC. All specimens were preserved in 37 ℃ water for 24 h, then SBS tests for eight specimens in each group were performed using a universal testing machine at a constant crosshead speed of 0.5 mm·min-1. The surface topography of one CRC of each group was observed using field emission scanning electron microscope（FE-SEM） at 100 amplification. The interface between CRC and GIC was observed using FE-SEM at 500 amplification. Then the nature of failure was also recorded using FE-SEM at 25 amplification and the data were analyzed with a Kruskal-Wallis H test. Results  The surface topography of each group and the interface  between CRC and GIC observed using FE-SEM were significantly different, but significant differences on the nature of failure between groups were not found（P>0.10）. SBS of each group was （4.28±0.18）MPa for RDB, （4.65±0.17）MPa for RDBE, （2.39±0.21）MPa for RDBA, respectively（P<0.01）.
Conclusion  The SBS between CRC and GIC is affected by the surface treatments of CRC.

Key words:  composite resin core, surface treatment, glass ionomer cement, shear bond strength